Influence of the pH on the synthesis of reduced graphene oxide under hydrothermal conditions
2012
Here we describe the important role played by the pH on the morphology and structure of the reduced graphite oxide (rGO) samples obtained by hydrothermal treatment of the previously prepared GO. The nature of the resulting samples has been studied on the basis of a complete battery of experimental techniques.
Cu-exchanged Al-rich SSZ-13 zeolite from organotemplate-free synthesis as NH3-SCR catalyst: Effects of Na+ ions on the activity and hydrothermal stab…
2017
Abstract The relatively low activity at lower temperatures and high cost of SSZ-13 zeolite from organotemplate synthesis are two of major problems of presently commercialized Cu-SSZ-13 catalysts for NH3-SCR reaction. Cu-exchanged Al-rich SSZ-13 catalysts with Si/Al = 4 from organotemplate-free synthesis have been prepared, and show superior NH3-SCR performance with NO conversions above 85% at wide-temperature window ranging from 150 to 650 °C. Cu-Na-SSZ-13 catalysts with varied amount of residual Na+ were prepared by partial ion-exchange of as-prepared Al-rich Na-SSZ-13, and it’s found that Cu-Na-SSZ-13 catalyst with moderate Na+ content can improve both the low-temperature activity and its…
Synthesis of single crystalline sub-micron rutile TiO2 rods using hydrothermal treatment in acidic media
2014
Size engineered rutile sub-micron rods were obtained from nanostructured titania under acidic conditions. The synthesis was performed by hydrothermal treatment starting from TiO2-P25 and HCl. The synthesis proceeds in less than two hours and can be up-scaled to several grams in a one-pot reaction by increasing the reaction time. The product is single-phase, and the particles are single crystalline as confirmed by electron diffraction and powder X-ray diffraction analysis. The length of the particles can be varied over a wide range from 100 nm to 1.3 μm by changing the acid concentration. Particle growth is proposed to proceed by a dissolution-recrystallization process via soluble [TiCl6]2− …
Caractérisation de poudres de zircone synthétisées par voie hydrothermale
1998
La synthese hydrothermale permet la realisation de poudres fines cristallisees et desagglomerees Ces qualites sont appropriees a l'elaboration de composites fins oxyde/oxyde par synthese simultanee des deux phases. Nous avons developpe ce protocole pour la realisation de nanocomposites ahrmine/zircone (Q). Nous presentons ici plus particulierement le travail effectue sur la zircone, Les conditions de traitement hydrothermal et d'un traitement thermique modere supplementaire sont analysees en relation avec les caracteristiques des poudres synthetisees. Differentes techniques complementaires sont utilisees pour ces poudres de zircone: diffraction des rayons X (% de la phase quadratique, taill…
Hydrothermal Processing for Increasing the Hydroxyl Ion Concentration in Hydroxyl Depleted Hydroxyapatite
2018
Thermal spraying is commercially used to produce hydroxyapatite coatings, but the high temperature depletes hydroxyl ions in the structure. To return hydroxyapatite to its original state, it is necessary to restore the hydroxyl ion content in the structure. In this work, the effect of hydrothermal treatment on the hydroxyl ions was investigated in hydroxyapatite powder and thermally sprayed hydroxyapatite coatings. Samples were hydrothermally treated at 200 °C for 24 h and 48 h. Chemical phases were determined by X-ray diffraction, functional groups and hydroxyl ion concentration was examined by Fourier transform infra-red spectroscopy. Results showed that hydrothermal processing of hydroxy…
Effect of hydrothermal time on the forming specific morphology of YPO4:Eu3+ nanoparticles for dedicated luminescent applications as optical markers
2023
A way to control the desired shape and microstructure of YPO4:Eu3+ nanoparticles through the precipitation method followed by a hydrothermal treatment is reported. This method is useful for achieving very high control over the YPO4:Eu3+ formation process with the selection of appropriate synthesis parameters. In detail, the autoclave processing time allows control of the shape and size of nano-needle-shaped particles independently in both directions, as confirmed by X-ray powder diffraction, FT-IR Spectroscopy and Electron Transmission Microscopy. In order to analyse the effect of the nanoparticles’ surroundings on the excitation and relaxation processes of luminescent ions, Eu3+ ion was us…
Water and temperature contribution to the structuration of starch matrices in the presence of flavour
2015
The effect of hydrothermal treatments and flavours addition on starch structure and its physical properties were studied. Native wheat starch was treated at 2 different hydrations (water-starch ratios: 50/50 and 80/20 g w/w) and temperatures (65 and 85 °C) in the presence of flavours (ethyl hexanoate and 2-hexanone). The freshly prepared samples were subjected to DSC and flavour analysis. Flavour inclusion complex could not be detected by DSC, however the result of flavour analysis proved that there were flavours interactions with starch. Both ethyl hexanoate and 2-hexanone interacted with starch at similar rates. The highest flavour loss was found in the samples at high hydration and heate…